High Strength Epoxy Mortar Resin - 100% Solids - Zero (0) VOC
Epoxy.com Product #28
Clear High Strength Epoxy Mortar Resin PRODUCT #28 is a
multipurpose colored epoxy binder for Epoxy Mortar Systems This all purpose epoxy resin is characterized as
an excellent general purpose material with good clarity and color retention. It
is essentially odorless and can therefore be used in occupied areas.
• Good troweling properties
• Excellent color retention
• Low odor for use in occupied areas.
• Low viscosity good wetting properties
• Available in "fast cure" systems.
• Minimum application temperature of 50°F (Contact Epoxy System, Inc.
for Low Temperature Cure).
• Substrate must be free of curing agents and any foreign materials.
• Slight color variation can be expected from batch to batch.
• Pigmented version should not be used as a coating.
100% solids amine cured Epoxy Resin.
Surface Preparation is the most critical portion to any
successful resinous flooring system application. All substrates must be properly
prepared as outlined in Epoxy.com Surface
Preparation Procedures. Work must be performed by trained or experienced
contractors or maintenance personnel. The Epoxy.com technical service
department is pleased to answer any questions.
Will vary with application method.
Clear to Slightly Amber
4A to I B by volume
minutes @ 70°F
950 cps, mixed approx.
10-20 mil film
Ultimate Cure 74°F
R-Recommended for continuous service. L-Limited
recommendation, occasional spills.
Methyl Ethyl Ketone
Tensile Strength ASTM-D-638
Adhesion to metal
Adhesion to concrete ACI Committee 403
350 p.s.i (concrete fails)
80 (Shore D)
Abrasion Resistance ASTM-C-501
35-40 mg loss (CS-17 wheel, 1 kg load, 1000 cycles)
Service Temperature MIL- D-3134F
160° F (immersion)
185°F (dry heat)
Impact Resistance MIL-D3134F § 4.7.3
Withstands 16ft/lbs. no cracking, delamination or chipping.
Indentation MIL-D-3134F § 4.7.4
Withstands 2,000 lbs./sq. in. for 30 min. without indentation.
Elevated Temperature Resistance MIL-D-31 34F §4 7 5
No slip or flow at required temperatures at 158 degrees F
Water Absorption ASTM-D-670-63 (24. hr. immersion)