Epoxy.com Product #640100% Solids Chemical and Heat Resistant CoatingDESCRIPTIONChemical & Heat Resistant Coating is a two component; highly cross linked Novolac, that is 100% solids. It can be brush, roll or airless spray applied coating designed to provide cavitation, corrosion and erosion resistance to concrete, metallic and nonmetallic surfaces. Epoxy.com PRODUCT #640 acts as an inert barrier against extremely harsh environmental factors such as low and high PH, temperature extremes, dry and fluid particulate flow and corrosive chemical attack. Link to related and similar products. Epoxy.com Product #640 Chemical and Heat Resistant epoxy supersedes Epoxy.com Product #634. USES
PHYSICAL PROPERTIES
CURED PROPERTIES
CHEMICAL RESISTANT PROPERTIESThe following represents percent flexural strength retained after two weeks cure at 770F followed by 30 days immersion in the chemical environment as described.
The following standards may be used in assessing what activities can be carried out after an application of PRODUCT #640.
Force cures may be used to either enhance chemical resistance or to allow the coating to be placed in service before 5 days. Allow a post cure of 12 to 24 hours before force curing. RECOMMENDED FORCE CURE SCHEDULE
NOTE: This product will cure well at temperatures as low as 40 - 450F. However, additional curing time must be provided. SURFACE PREPARATIONCONCRETE: Surface must be clean and sound. Remove all dirt, laitance, grease curing compounds and other foreign matter by sandblasting, mechanical abrasion. If acid etching is used follow with abrasive or mechanical abrasion. Remove water and dust from all surfaces with an oil free blast, or vacuum, immediately prior to application. STEEL: Prior to sand blasting remove all grease, dirt and other contaminants from the surface. Grind sharp edges to a minimum radius of 1/8 inch. Remove all weld splatters. Sandblast to a white metal finish according to SSPC-SP-5-63 or NACE standard TM-01-70 with a minimum anchor profile of 3 mils. MIXINGMix ratio is two parts by volume base ("A") to one part by volume hardener ("B"). APPLICATIONPRODUCT #640 can be applied by brush, roller or airless spray equipment. PRODUCT #640 is designed to be spray applied at 10 to 15 mils per coat. Relative humidity during the coating process should be a maximum of 90% for application to commence. A minimum of two coats is recommended. If the second coat is applied before the first coat cures, no surface preparation is required. Simply apply the second coat maintaining the required mils per coat. However, if the first coat has cured more than 24 hours, the first coat must be brush blasted prior to the second coat. CLEANINGClean all equipment immediately after use with MEK or acetone. CAUTIONWARNING! A Component contains epoxy resin. DANGER! B Component contains alkaline amines; strong sensitizer. May cause skin sensitization or other allergic responses. Use with good ventilation, particularly if material is heated or sprayed. Prevent all contact with skin or eyes. Wear protective clothing, goggles, gloves and/or barrier creams. Keep container closed when not in use. Wash thoroughly after handling. FIRST AID: In case of skin contact, immediately wash with soap and water. In case of eye contact, flush eyes with copious amounts of water for at least fifteen (15) minutes. Remove contaminated clothing and shoes. If irritation persists, seek medical attention. Wash clothing before reuse. FOR INDUSTRIAL USE ONLY KEEP AWAY FROM CHILDREN Other customers who visited this page also visited:
|
|